Static friction, surface roughness, and antibacterial activity of orthodontic brackets coated with silver and silver chitosan nanoparticles.

BACKGROUND

To determine the effect of silver and silver chitosan nanocoatings on monocrystalline ceramic, polycrystalline ceramic, and metallic brackets regarding friction, roughness, and antibacterial effect against Streptococcus mutans.

METHODS

A total of 99 upper right premolar brackets with a 0.022 × 0.025 -inch slot were divided into three groups, each 33 according to coating material; the non-coated group, silver nanoparticles (AgNPs), and silver chitosan nanoparticles (Ag-CsNPs) groups. Each group was equally subdivided into the following three subgroups regarding bracket materials: monocrystalline ceramic, polycrystalline ceramic, and metallic brackets. A universal testing machine determined static friction on a custom-made acrylic jig. Then a profilometer machine was used to collect roughness data, and finally, the anti-cariogenic effect was measured with the disc diffusion technique's "minimum zone of inhibition" against Streptococcus mutans. Two-way ANOVA was used to compare data between groups and subgroups, followed by the Bonferroni test for multiple pair-wise comparisons.

RESULTS

The nanocoating effect on ceramic brackets' static friction was non-significant. The AgNPs and Ag-CsNPs coated metallic group revealed a significant increase in static friction-a significant effect of the nanocoating in the surface roughness of monocrystalline and polycrystalline ceramic brackets. A significant favorable effect of AgNPs and Ag-CsNPs against Streptococcus mutans was observed.

CONCLUSIONS

AgNPs and Ag-CsNPs coats are unsuitable for decreasing friction in metallic brackets or improving roughness in polycrystalline ceramic brackets. Nano coating can improve roughness in monocrystalline ceramic brackets. Coating brackets with AgNPs and Ag-CsNPs has a tremendous antibacterial effect on Streptococcus mutans, a substantial factor in the incidence of dental caries.